Experiments for specific heat [J/(kg K)], or heat capacity, were conducted using a heat flow meter on unconditioned and dried samples at 10 °C, 20 °C, 30 °C and 40 °C.

Experiments for thermal conductivity [k] were conducted using a heat flow meter on unconditioned samples at 15 °C and 45 °C.

Mass loss rate [kg/s] was measured in cone calorimeter experiments at three heat fluxes: 25 kW/m², 50 kW/m², and 75 kW/m².

This material is not combustible. One test per heat flux level was conducted for a duration of 30 minutes. The other replicates were conducted for only 10 minutes based on the observation that no significant mass loss occurred after this time in the first replicates.

Experiments for heat release per unit area [kW/m²] were conducted on samples conditioned at 20°C and 50% relative humidity using a cone calorimeter at three different heat fluxes: 25 kW/m², 50 kW/m², and 75 kW/m².

This material is not combustible. One test per heat flux level was conducted for a duration of 30 minutes. The other replicates were conducted for only 10 minutes based on the observation that no significant mass loss occurred after this time in the first replicates.

Carbon monoxide yield was measured during cone calorimeter experiments conducted at heat fluxes of 25 kW/m², 50 kW/m², and 75 kW/m².

This material is not combustible. One test per heat flux level was conducted for a duration of 30 minutes. The other replicates were conducted for only 10 minutes based on the observation that no significant mass loss occurred after this time in the first replicates.

Experiments for specific heat release rate [W/g], were conducted using a micro-scale combustion calorimeter at a heating rate of 30 K/min.

Effective heat of combustion [MJ/kg] is calculated from data collected in both micro-scale combustion calorimeter experiments and cone calorimeter experiments.

Cone Calorimeter Test Notes:
This material is not combustible. One test per heat flux level was conducted for a duration of 30 minutes. The other replicates were conducted for only 10 minutes based on the observation that no significant mass loss occurred after this time in the first replicates.